| 特性級(jí)別 | 增強(qiáng)級(jí)|||標(biāo)準(zhǔn)級(jí)||| |
| 牌號(hào) | LGF40 |
| 加工級(jí)別 | 涂覆級(jí)|||拉絲級(jí)|||唰出級(jí)|||吹墮級(jí)||| |
| 品名 | TPU-聚脂 LGF40 美國(guó)陶氏 |
| 廠家(產(chǎn)地) | 美國(guó)陶氏 |
| 用途級(jí)別 | 通用級(jí)||| |
TPU-聚脂 LGF40 陶氏
生產(chǎn)企業(yè)：陶氏
規(guī)格用途
| 規(guī)格級(jí)別 | 外觀顏色 | ||
| 該料用途 | |||
| 備注說明 | |||
技術(shù)參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重2 | ASTMD792 | 1.21 | g/cm3 | |
| 物理性能 | 密度3 | DIN53479 | 1.20 | g/cm3 | |
| 物理性能 | MeltVolume-FlowRate(MVR)(190°C/10.0kg) | 60.0 | cm3/10min | ||
| 物理性能 | 收縮率-流動(dòng)(注塑) | ASTMD955 | 0.40 | % | |
| 機(jī)械性能 | Abrasion2 | DIN53516 | 20 | mm3 | |
| ELASTOMERS | 彈性體 | TestMethod | NominalValue | Unit | |
| ELASTOMERS | TensileStress3(100%Strain,0.635mm) | ASTMD412 | 4.69 | MPa | |
| ELASTOMERS | TensileStress3(100%Strain,0.635mm) | DIN53504 | 8.50 | MPa | |
| ELASTOMERS | TensileStress3(300%Strain,0.635mm) | ASTMD412 | 10.3 | MPa | |
| ELASTOMERS | TensileStress3(300%Strain,0.635mm) | DIN53504 | 16.0 | MPa | |
| ELASTOMERS | TensileStrength3(Break,0.635mm) | ASTMD412 | 37.9 | MPa | |
| ELASTOMERS | TensileStress3(Break,0.635mm) | DIN53504 | 36.0 | MPa | |
| ELASTOMERS | TensileElongation3(Break,0.635mm) | ASTMD412 | 570 | % | |
| ELASTOMERS | TensileElongation3(Break,0.635mm) | DIN53504 | 600 | % | |
| ELASTOMERS | TearStrength3(0.635mm) | ASTMD624 | 80.6 | kN/m | |
| ELASTOMERS | TearStrength3(0.635mm) | DIN53515 | 83 | kN/m | |
| ELASTOMERS | 壓縮*變形2 | 23°C,24hr | ASTMD395 | 25 | % |
| ELASTOMERS | 壓縮*變形2 | 70°C,24hr | ASTMD395 | 40 | % |
| ELASTOMERS | 壓縮*變形2 | 23°C,24hr | DIN53517 | 25 | % |
| ELASTOMERS | 壓縮*變形2 | 70°C,24hr | DIN53517 | 0.40 | % |
| ELASTOMERS | 壓縮*變形2 | 巴肖氏彈性 | DIN53517 | 1 | % |
| 硬度 | 肖氏硬度 | 邵氏A,注塑 | ASTMD2240 | 90 | |
| 硬度 | 肖氏硬度 | 邵氏D,注塑 | ASTMD2240 | 38 | |
| 硬度 | 肖氏硬度 | 邵氏A,注塑 | DIN53505 | 90 | |
| 硬度 | 肖氏硬度 | 邵氏D,注塑 | DIN53505 | 38 | |
| 熱性能 | TMA2 | High | InternalMethod | 170 | °C |
| 熱性能 | TMA2 | Low | InternalMethod | 125 | °C |
TPU-聚脂 LGF40 陶氏